RA333
RA333
RA333® alloy is a high chromium nickel base superalloy with outstanding resistance to high temperature oxidation and carburization. RA333 has an exceptional ability to withstand the repeated thermal shock of oil or water quenching. RA333 is one of the few materials that can withstand corrosive conditions ranging from aqueous to white heat. Upon shutdown, RA333 resists dew point corrosion by sulfuric acid and polythionic acid stress corrosion cracking.
Weld RA333 with matching composition N06333 bare wire or RA333-70-16 AC/DC coated electrodes. Do not preheat, keep interpass temperature below 212°F and use reinforced stringer beads. Machinability rating of RA333 is 12-15% of B1112; turn 20-25 sfm with high speed steel tools.
Applications
- Tube supports in refineries and coal fired boilers
- Heat treating muffles, retorts, fan shafts and fixtures
- Carbon Fiber production muffles
- Sulfuric acid plant stack dampers
- Molten glass spinnerets
- Flare tips
- RA333 weld filler for repair welding of cast heat resistant alloys
- Tire Drop Chutes for Cement Kilns
Specifications
- AMS 5593, AMS 5717
- ASTM B 718, ASTM B 719, ASTM B 722, ASTM B 723, ASTM B 726
- UNS N06333
- W. NR./EN 2.4608
| Nominal Chemical Composition (%) | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| Ni | Cr | Mo | Co | W | Si | Mn | C | Fe | |
| MIN | 44.00 | 24.00 | 2.50 | 2.50 | 2.50 | 0.75 | – | – | – |
| MAX | 47.00 | 27.00 | 4.00 | 4.00 | 4.00 | 1.50 | 2.00 | 0.08 | Bal |