INCOLOY® Filler Metal 65
INCOLOY® Filler Metal 65 is used for gas-tungsten-arc welding of INCOLOY® alloy 825 and other nickel-iron-chromium-molybdenum-copper alloys of similar composition. The weld metal is highly corrosion resistant, particularly in reducing chemicals such as sulphuric and phosphoric acids. INCOLOY® Filler Metal 65 can also be used for depositing overlays on carbon and low alloys steels.
Specifications:
- AWS A5.14 ERNiFeCr-1 (UNS N08065)
- ASME II, Part C, SFA-5.14, ERNiFeCr-1 (UNS N08065)
- ASME IX, F-No.45
- BS 2901 NA 41
- (EN) ISO 18274-SNi8065 (NiFe30Cr21Mo3)
For manufacture to ASME III (NCA3800, NB2400), Rolls Royce, AMS and other specifications please refer your inquiry to the Technical Department prior to order placement.
| Nominal Chemical Composition (%) |
| Ni+Co |
C |
Mn |
Fe |
S |
Si |
Cu |
Cr |
Al |
Ti |
Mo |
P |
Others |
| 38.0-46.0 |
0.05 max |
1.0 max |
22.0 min |
0.03 max |
0.50 max |
1.5-3.0 |
19.5-23.5 |
0.20 max |
0.60-1.20 |
2.50-3.50 |
0.03 max |
0.50 max |
| Minimum Mechanical Properties |
| Tensile Strength (psi) |
80,000 |
| Tensile Strength (MPA) |
552 |
| Elongation (4d) % |
25 |
HAYNES® 825® RTW™ Filler Metal
HAYNES® 825 RTW™ Filler Metal is used for the gas metal arc and gas tungsten arc welding of alloy 825 and other alloys of similar composition. The weld metal is often used as a corrosion-resistant overlay on carbon and low alloy steels. The corrosion-resistant overlay preforms well in oil and gas applications as well as reducing eniornments like sulphuric and phosphoric acids. The RTW™ finish on the spooled wire promotes smooth feeding through welding equipment and reduced tip wear in contact tips.
Specifications:
- AMS A5.14 ERNiFeCr-1
- ASME SFA-5.14 ERNiFeCr-1
- UNS N08065
- ASME IX, F-No.45
| Nominal Chemical Composition (%) |
| Ni+Co
|
Cr
|
Fe
|
Mo
|
Cu
|
Ti
|
Mn
|
Si
|
Other
|
Al
|
S
|
P
|
C
|
| 38.0-46.0 |
19.5-23.5 |
22.0 min |
2.5-3.5 |
1.5-3.0 |
0.6-1.2 |
1.0 max |
0.50 max |
0.50 max |
0.20 max |
0.03 max |
0.03 max |
0.05 max |
| Minimum Mechanical Properties |
| Tensile Strength (psi) |
80,000 |
| Tensile Strength (MPA) |
552 |
| Elongation (4d) % |
25 |