AWS A5.28 Low-Alloy Steel Electrodes & Rods for Gas Shielded Arc Welding
ER70S-B2L
ER70S-B2L [ER49S-B2L] are identical to type ER80S-B2 [ER55S-B2] except for the low-carbon content (0.05 percent maximum) and thus the lower strength levels. This also reduces hardness and under some conditions improves corrosion resistance. This alloy exhibits greater resistance to cracking and is more suitable for welds to be left in the as-welded condition or when the accuracy of the postweld heat treatment operation is questionable. This classification was previously ER80S-B2L in the A5.28-79 specification. The strength requirements and classification designator have been changed to reflect the true strength capabilities of the chemical composition.
ER80S-B2
ER80S-B2 [ER55S-B2] are used to weld ½Cr-½Mo, 1Cr-½Mo, and 1-¼Cr-½Mo steels for elevated temperatures and corrosive service. They are also used for joining dissimilar combinations of Cr-Mo and carbon steels. All transfer modes of the GMAW process may be used. Careful control of preheat, interpass temperatures, and postheat is essential to avoid cracking. These electrodes are classified after postweld heat treatment. Special care must be used when using them in the as-welded condition due to higher strength levels.
ER80S-B3L
ER80S-B3L [ER55-B3L] are identical to type ER90S-B3 [ER62S-B3] except for the low-carbon content (0.05 percent maximum) and, therefore, the lower strength levels. These alloys exhibit greater resistance to cracking and are more suitable for welds to be left in the as-welded condition. This classification was previously ER90S-B3L in the AWS A5.28-79 specification. The strength requirements and classification designator have been changed to reflect the true strength capabilities of the chemical composition.
ER80S-B6
ER80S-B6 [ER55S-B6] contains about 4.5 to 6.0 percent chromium and about 0.5 percent molybdenum. It is used for welding material of similar composition, usually in the form of pipe or tubing. This alloy is an air-hardening material and, therefore, when welding with this filler metal, preheat and postweld heat treatment are required. This electrode is similar to that previously classified as ER502 in AWS A5.9-93.
ER80S-B8
ER80S-B8 [ER55S-B8] contains 8.0 to 10.5 percent chromium and about 1.0 percent molybdenum. Filler metal of this classification is used for welding base metal of similar compositions, usually in the form of pipe or tubing. The alloy is an air-hardening material, and therefore, when welding with this filler metal, preheating, and postweld heat treatment are required. This electrode is similar to that previously classified as ER505 in AWS A5.9-93.
ER80S-D2
ER80S-D2 [ER55S-D2] and ER90S-D2 [ER62S-D2] classifications have the same chemical requirements as the E70S-1B classification of AWS A5.18-69. The differences between the ER80S-D2 and the ER90S-D2 classifications are the change in shielding gas and the mechanical property requirements. Filler metals of these classifications contain molybdenum for increased strength and a high level of deoxidizers (Mn and Si) to control porosity when welding with CO2 (AWS A5.32 Class SG-C) as the shielding gas. They will give radiographic quality welds with excellent bead appearance in both ordinary and difficult-to-weld carbon and low-alloy steels. They exhibit excellent out-of-position welding characteristics with the short circuiting and pulsed arc processes.
The combination of weld soundness and strength makes filler metals of these classifications suitable for single- and multiple-pass welding of a variety of carbon and low-alloy, higher strength steels in both the as-welded and postweld heat-treated conditions. The chemical composition of these classifications differs from those of the “-D2” type electrodes in AWS A5.5.
ER90S-B3
ER90S-B3 [ER62S-B3] is used to weld 2-¼Cr-1Mo steels used for high-temperature/high-pressure piping and pressure vessels. These may also be used for joining combinations of Cr-Mo and carbon steel. All GMAW modes may be used. Careful control of preheat, interpass temperatures, and postweld heat treatment is essential to avoid cracking. These electrodes are classified after postweld heat treatment. Special care must be used when using them in the as-welded condition due to higher strength levels.
ER90S-D2
ER90S-D2 [ER62S-D2] and ER80S-D2 [ER55S-D2] classifications have the same chemical requirements as the E70S-1B classification of AWS A5.18-69. The differences between the ER80S-D2 and the ER90S-D2 classifications are the change in shielding gas and the mechanical property requirements. Filler metals of these classifications contain molybdenum for increased strength and a high level of deoxidizers (Mn and Si) to control porosity when welding with CO2 (AWS A5.32 Class SG-C) as the shielding gas. They will give radiographic quality welds with excellent bead appearance in both ordinary and difficult-to-weld carbon and low-alloy steels. They exhibit excellent out-of-position welding characteristics with the short circuiting and pulsed arc processes.
The combination of weld soundness and strength makes filler metals of these classifications suitable for single- and multiple-pass welding of a variety of carbon and low-alloy, higher strength steels in both the as-welded and postweld heat-treated conditions. The chemical composition of these classifications differs from those of the “-D2” type electrodes in AWS A5.5.
ER100S-1
ER100S-1 [ER69S-1] deposit high-strength, very tough weld metal for critical applications. Originally developed for welding HY-80 and HY-100 steels for military applications, they are also used for a variety of structural applications where tensile strength requirements exceed 100 ksi [690 MPa], and excellent toughness is required to temperatures as low as -60°F [-50°C]. Mechanical properties obtained from weld deposits made with electrodes of these classifications will vary depending on the heat input used.
ER110S-1
ER110S-1 [ER76S-1] deposit high-strength, very tough weld metal for critical applications. Originally developed for welding HY-80 and HY-100 steels for military applications, they are also used for a variety of structural applications where tensile strength requirements exceed 100 ksi [690 MPa], and excellent toughness is required to temperatures as low as -60°F [-50°C]. Mechanical properties obtained from weld deposits made with electrodes of these classifications will vary depending on the heat input used.
ER120S-1
ER120S-1 [ER83S-1] deposit high-strength, very tough weld metal for critical applications. Originally developed for welding HY-80 and HY-100 steels for military applications, they are also used for a variety of structural applications where tensile strength requirements exceed 100 ksi [690 MPa], and excellent toughness is required to temperatures as low as -60°F [-50°C]. Mechanical properties obtained from weld deposits made with electrodes of these classifications will vary depending on the heat input used.